Permanently elastic silicone sealing compounds for engine and bodywork with excellent adhesion Contents: 70 ml Chemical basis: Oxime-curing sealant Density/conditions: 0.97 g/cm / at 20C Full curing speed: 1.5 mm/d Colour: Transparent Smell/fragrance: Characteristic Weight of content: 100 g Min. skin-formation time: 8 min Max. skin-formation time: 15 min Conditions for skin-formation time: at 23C and 50% relative humidity Shore A hardness: 18 Elongation at break: 300 % Continuous motion absorption (up to 150C): 25 % Continuous motion absorption (above 150C): 18 % Min./max. temperature resistance: -50 to 150 C Max. short-term temperature resistance: 180 C Min./max. processing temperature: 5 to 60 C Shelf life from production: 18 Month Conditions to maintain shelf life from production: cool and dry storage area below 25C Cold-vulcanising silicone rubber Bridges larger unevenness Reliable at sealing, even after withstanding years of vibrations Does not run or pull threads Excellent adhesion and chemical resistance Skin formation after just a few minutes, vulcanisation rate approx. 1.5 mm/day The usage instructions are recommendations based on the tests we have conducted and based on our experience; carry out your own tests before each application. Due to the large number of applications and storage and processing conditions, we do not assume any liability for a specific application result. Insofar as our free customer service provides technical information or acts as an advisory service, no responsibility is assumed by this service except where the advice or information given falls within the scope of our specified, contractually agreed service or the advisor was acting deliberately. We guarantee consistent quality of our products. We reserve the right to make technical changes and further develop products.